Influence of thermo-mechanical history on the ordering kinetics in 18 carat Au alloys

Precious alloys are subjected to a series of mechanical and thermal operations during manufacturing. For 18 carat gold alloys the processing operations can induce L10 ordered nanodomains, known to lead to the build-up of residual stresses, which are the prime cause for shape distortion. Here, in situ high-energy synchrotron X-ray diffraction experiments in combination with electron microscopy observations reveal the influence of the thermo-mechanical history and chemical composition on the ordering kinetics during isochronal heating. Initially, during heating, the elastic lattice strain in the ordered nanodomains increases. The ordering rate and accumulation of lattice strain depend on the cooling rate, predeformation and chemical composition. Above a given temperature, which depends on the deformation state and chemical composition, the lattice strain in the ordered domains relaxes which is ascribed to the formation of a tweed structure.

Source: Acta Materialia


Nos prochaines manifestations

Affiche CIC2022
  • 28.09.2022 - SwissTech Convention Center, Lausanne et en ligne

CIC2022 - Entre rêves, réalités et nécessités, comment l'horlogerie ajuste son amplitude sans perdre ses repères?

Le programme du CIC2022 est disponible.

L'application SSC

Suivez en direct les actualités de notre société sur votre smartphone. Recevez en exclusivité les informations importantes grâce à la notification intégrée.

  • Télécharger notre application sur l'App Store
  • Télécharger notre application sur Google Play