Understanding variant selection and texture in additively manufactured red-gold alloys

Printing gold alloys parts is a challenge due to the high reflectivity and thermal conductivity of these materials. Recent studies show an improvement in printing gold using the Laser Powder Bed Fusion (L-PBF) process; however, the impact of the A1→L10 phase transformation on printed red-gold alloy has not been studied. In this work, 3D printed red-gold samples with different post-processing conditions have been heat-treated at 250 °C to investigate the effect of the sample stress states on variant selection, by Electron Backscatter Diffraction. Synchrotron X-ray diffraction experiments reveal the presence of a non-negligible amount of tetragonal phase in the as-build red-gold samples. The use of an intermediate heat treatment at 600 °C to eliminate small domains of tetragonal phase formed during the manufacturing process demonstrates that the crystallographic textures following heat treatment are highly dependent on the stress-state during the early stage of the phase transformation.

Source: Scripta Materialia

Link: https://www.sciencedirect.com/science/article/pii/S1359646221007697

L'application SSC

Suivez en direct les actualités de notre société sur votre smartphone. Recevez en exclusivité les informations importantes grâce à la notification intégrée.

  • Télécharger notre application sur l'App Store
  • Télécharger notre application sur Google Play